JIC DAIPALITE / Industrial Thermal Insulation
650°C+High-temperature insulation
Integral Technology provides JIC DAIPALITE industrial insulation for high-temperature equipment, piping and furnace applications, helping reduce heat loss, maintain process temperature and coordinate material with installation planning.
A stable insulation layer for high-temperature equipment
DAIPALITE is based on Xonotlite calcium silicate and is used for industrial equipment and piping insulation. JIC’s official data lists a maximum service temperature of 1000°C for DAIPALITE-E; DAIPALITE-E 1100 is positioned for furnace backup insulation where the market requires resistance above 1000°C.
Product families and selection direction
DAIPALITE-E
JIS A 9510 Type 1-15 series for industrial equipment and piping insulation.
DAIPALITE-Ei
Water-repellent series evaluated against the service environment and installation conditions.
DAIPALITE-EA / EiA
ASTM-aligned product families for project-specific selection.
DAIPALITE-E 1100
For furnace backup insulation and market requirements above 1000°C, according to JIC’s public release.
DAIPALITE-WPA
Ultra-lightweight with water-repellent properties throughout the material, for piping, towers and tanks.
Material characteristics
- Inorganic Xonotlite calcium silicate
- Asbestos-free and non-combustible material characteristics
- Low-density, heat-resistant and low-thermal-conductivity direction
- Pre-formed or fabricated pipe covers, elbows, boards and equipment shapes
- JIC official data lists DAIPALITE-E maximum service temperature at 1000°C
Typical applications
- Petrochemical and refinery equipment
- Power-plant boilers and steam turbines
- Gas turbines and exhaust piping
- High-temperature industrial piping and elbows
- Tanks, furnaces and equipment shells
- Furnace backup insulation
- LNG and related equipment
- Pipe supports and pre-formed parts
Public specification summary
| Base material | Xonotlite calcium silicate |
|---|---|
| DAIPALITE-E maximum service temperature | 1000°C (JIC official product data) |
| Standards | JIS A 9510 Type 1-15; selected families aligned with ASTM C533 Type I |
| Forms | Pipe covers, boards, elbows and equipment-specific pre-formed parts |
| Selection | Operating temperature, pipe size, thickness, environment, mechanical load and installation method |
Final product specifications, dimensions, thickness and supply model follow JIC’s latest documentation and project conditions.
Start with the equipment temperature
Share application, operating temperature, pipe dimensions, insulation thickness and site constraints. Integral can help assess JIC DAIPALITE materials and installation integration.
Official sources: JIC DAIPALITE-E product data, DAIPALITE-E 1100 release, and JIC Vietnam product page.
Temperature comparison
Above 650°C: heat resistance in the material structure
JIC’s catalog compares crystal structures: Tobermorite-based calcium silicate insulation is generally used up to 650°C, while the Xonotlite-based DAIPALITE-E series retains its shape up to 1000°C. After heating at 1000°C for three hours, maximum linear shrinkage is listed as 2.0%.
Select by model, equipment temperature, thickness and service conditions. The comparison comes from JIC’s catalog and does not mean every family has the same specification.
Water-repellent / CUI
Water repellency and CUI countermeasures
JIC’s water-repellent DAIPALITE-EiA and DAIPALITE-E products are impregnated with a special corrosion inhibitor. Their water-repellent function and chemical effect contribute to countermeasures for Corrosion Under Insulation (CUI). DAIPALITE-WPA is an ultra-lightweight calcium silicate insulation material with water-repellent properties throughout the material, for piping, towers and tanks.
Water-repellent does not mean waterproof. Joints, cut surfaces, jacketing and construction management must follow the formal installation requirements.
Industrial thermal management
- Oil refining, petrochemical and power facilities
- Piping, towers, tanks and equipment shells
- CUI assessment for water-repellent product families
- Product selection around environment and insulation construction
Environmental process
Rice-husk resources in the process
JIC states that the DAIPALITE-E series is manufactured at JIC Vietnam using rice-husk boiler energy for reaction and drying, while rice-husk ash is used as a high-purity raw material. The process is designed to reduce environmental impact while equipment insulation improves plant thermal efficiency.
New property summary
| DAIPALITE-EA | Apparent density 170 kg/m³; flexural strength ≥344 kPa; compressive strength ≥688 kPa; maximum service temperature 1000°C |
|---|---|
| DAIPALITE-E | Apparent density ≤155 kg/m³; flexural strength ≥200 kPa; compressive strength ≥300 kPa; maximum service temperature 1000°C |
| DAIPALITE-WPA | Ultra-lightweight with water-repellent properties throughout the material; for piping, towers and tanks |
Values and product descriptions are summarized from the new JIC catalog and technical data sheet in this project. Final specifications, test conditions, supply models and engineering scope follow the latest documentation and project confirmation.